TECHNICAL SPECIFICATIONS
| Base Composition | Premium Hydrated Dolomite combined with unique self-bonding polymers and anti-cracking micro-additives. |
| Physical State & Color | Dry, ultra-pure homogenous powder. Superior High-Lux Brilliant White. |
| Optical Brightness / Reflectance | 94% + via standard Reflectance Method (Outperforming the standard 90% industry ceiling) |
| Dry Powder Bulk Density | 0.60 gm/cc to 0.65 gm/cc (Ensuring optimized powder yield and light brush drag). |
| Recommended Mix Fluid Ratio | 1 part FESTON PLUS powder to 2 parts clean water by volume (1 kg powder to 2 Liters water |
| Slurry Pot Life Stability | Up to 6 Hours (Providing extended on-site workability over competitive 4-hour baselines). |
| Initial Drying Time (Touch Dry) | 30 Minutes minimum at ambient room temperature (27°C). |
| Inter-Coat Re-coat Window | 6 to 8 Hours minimum depending on localized ambient humidity and air current layout. |
| Final Structural Setting Time | 24 Hours maximum for full, uniform molecular crystallization |
| Fineness / Sieve Graduation | Precisely graded lime and dolomite powder with 100% mass passing a fine 300 mesh sieve. |
| Enhanced Structural Adhesion | Self-Bonding Matrix. Does not require external water curing postbrushing. |
| Volatile Organic Compounds (VOC) | 0% / Absolute Zero VOC Formulation. |
| Estimated Area Coverage | 140 to 160 Sq.ft / kg / coat (13.5 to 14.8 Sq.meters/kg/coat) depending on surface profile. |
| Recommended Substrates | All cured porous cement plaster, masonry walls, ceilings, and raw concrete sections. |
| Application Methodology | Optimized exclusively for masonry block brush application to ensure flawless coat uniformity. |
| Packaging & Size Framework | Available in heavy-duty moisture-proof multi-ply 5 Kg, 10 Kg, and 25 Kg HDPE bags. |
Paint Master FESTON PLUS Base Coat is a high-performance, dry powder technical undercoat optimized for all cured, porous interior and exterior masonry surfaces. While ordinary white cement base coats shrink, crack, or wash away under heavy moisture, FESTON PLUS is fortified with special mineral additives and advanced molecular binders that fuse directly with cementitious substrates. It operates both as an elite anti-porosity sealer and a luxurious, high-whiteness structural foundation, establishing a perfectly uniform, buttery-smooth matte topography that enhances the true tone of any architectural topcoat.
Frequently Asked Questions
FESTON PLUS introduces a 6X structural strength threshold and up to 160% more area coverage compared to white cement baselines. Unlike traditional primers that simply sit on top of walls as a film, FESTON PLUS leverages an advanced dolomite self-bonding matrix that sinks into and crosslinks within masonry pores, permanently blocking peeling, flaking, and chalking while saving substantial quantities of topcoat paint.
The recommended technical ratio is 1:2 by volume. Add 1 kg of FESTON PLUS powder into 2 Liters of clean water. For absolute homogeneity, mix preferably with a low-speed mechanical stirrer until a uniform, lump-free slurry is created. Keep the slurry lightly stirred during use to avoid particle settling.
FESTON PLUS is precision-engineered for dense base coat integration. Applying it with a highquality masonry block brush allows the applicator to mechanically work the micro-particles directly into structural hairline cracks, pores, and micro-cavities. Roller application on unprimed masonry can pull on the wet slurry, resulting in uneven coating thicknesses and microscopic voids.
No. Thanks to the advanced chemical self-bonding formulation, FESTON PLUS sets flawlessly through natural atmospheric moisture balancing and requires absolutely zero manual water-curing spray sequences after brush application. However, make sure that newly constructed cement plasters have completed their baseline 28-day water curing window before applying any base coat.
No. FESTON PLUS is a highly targeted crystalline mineral compound optimized exclusively for porous masonry structures (cement plaster, internal ceilings, brickwork, and cast concrete). It is not formulated to bond with non-porous or flexible industrial materials such as wood, iron, steel, or synthetic plastics.